端羟基聚环氧氯丙烷酯化反应研究  

Study on Esterification of Hydroxyl-Terminated Polyepichlorohydrin

作　　者：王静刚[1] 李俊贤[2] 王勃[2] 

机构地区：[1]河南科技大学,河南洛阳471003 [2]黎明化工研究院,河南洛阳471000

出　　处：《化学推进剂与高分子材料》2008年第4期23-26,共4页Chemical Propellants & Polymeric Materials

摘　　要：通过端羟基聚环氧氯丙烷(PECH)的酯化,合成了端酯基PECH,用FT-IR和NMR进行了结构表征。优化了酯化反应工艺,结果表明:以乙酸酐为酯化剂,酯化剂与羟基物质的量比为1.6;N-甲基咪唑为催化剂,催化剂质量分数为3.6%;1,2-二氯乙烷为溶剂,反应温度为80℃,反应时间为0.5h,则羟基转化率为100%,收率>94.3%。Ester-terminated polyepichlorohydrin was synthesized by esterification of hydroxyl-terminated polyepichlorohydrin and the structures were charactered by FT-IR and NMR. The optimal reaction conditions ofesterification was investigated. The result shows that the conversion of hydroxyl is 100% and product yield 〉 94.3% when acetic anhydride is used as esterifying agent, the molar ratio of esterifying agent to hydroxy group is 1.6, N-methyl imidazole is used as esterification catalyst, the mass fraction of the catalyst is 3.6%, 1,2-dichloroethane is used as solvent, reaction temperature is 80℃, reaction time is 0.5 h.

关 键 词：聚环氧氯丙烷 酯化 增塑剂 

分 类 号：TQ414[化学工程]