弯曲载荷下涂层断裂行为  被引量:2

Fracture behavior of coatings under bend loading

在线阅读下载全文

作  者:马崇[1] 荆洪阳[2] 徐连勇[2] 白树海[3] 

机构地区:[1]天津市电力公司技术中心,300040 [2]天津大学材料科学与工程学院,300072 [3]天津市滨海市政建设发展有限公司,300050

出  处:《焊接》2008年第4期34-38,共5页Welding & Joining

基  金:新世纪优秀人才支持计划;教育部博士点基金(20050056035);教育部博士点基金新教师资助项目(20070056096)

摘  要:采用静载下的三点弯曲试验,详细分析观察了高速电弧喷涂LX88A金属基陶瓷涂层的断裂行为。研究发现涂层中某位置所受力矩达到一定值时,该处会产生垂直于界面的裂纹,故可将力矩是否达到临界值作为该位置产生裂纹的条件。有限元分析结果也证明了上述结论,对于三个不同位置的裂纹,当裂纹产生时该位置处界面附近的应力水平基本接近。研究结果可以为涂层构件的设计提供参考。The fracture behavior of LX88A metal-based ceramic coatings by high velocity arc spraying technology in 3-point bend specimens had been observed.It was found that the crack normal to the interface in the coatings occurrs where a fixed moment of force was reached.So whether the moment reached to the critical value or not can be used as the condition of crack occurrence.The finite element analysis results proved the previous conclusion.The stress levels at the three different locations where the cracks occurred near the interface almost were same.The results will provide the help for the design of coatings and the structure integrity evaluation of coatings/substrates systems.

关 键 词:涂层 界面 断裂行为 有限元分析 

分 类 号:TG115.28[金属学及工艺—物理冶金]

 

参考文献:

正在载入数据...

 

二级参考文献:

正在载入数据...

 

耦合文献:

正在载入数据...

 

引证文献:

正在载入数据...

 

二级引证文献:

正在载入数据...

 

同被引文献:

正在载入数据...

 

相关期刊文献:

正在载入数据...

相关的主题
相关的作者对象
相关的机构对象