浇注温度对ADC12合金超低速压铸件组织性能的影响  

Effects of Injection Temperature on Microstructure and Mechanical Properties of ADC12 Aluminum Alloy in Super Slow Speed Die Casting

作　　者：纪莲清[1] 纪培英[1] 熊守美[2] 村上正幸[3] 松本悦豪[3] 池田伸吾[3] 

机构地区：[1]郑州轻工业学院机电工程学院 [2]清华大学机械工程系 [3]日本东洋机械金属株式会社

出　　处：《特种铸造及有色合金》2008年第7期529-531,共3页Special Casting & Nonferrous Alloys

摘　　要：应用简单圆形拉伸试样,研究了浇注温度对ADC12铝合金超低速压铸件性能的影响,以优化超低速压铸工艺及其参数。试验结果表明,在超低速试验条件下,各种浇注温度下铸件的密度都比普通压铸要高;浇注温度有最佳值,最佳值的大小和模具温度、脱模剂有关。在超低速基准试验条件下,浇注温度的最佳值为700℃,此时合金中的初生α-Al为树枝晶状,与较高浇注温度时相比,一次和二次枝晶臂明显变小或变短,铸件性能较高。In order to optimize the super slow speed (SSS) die casting process, effects of pouring temperature on mechanical properties of ADC12 magnesium alloy in SSS die casting were examined with a standard tensile testing specimen. The results show that the density of specimen in SSS die casting is higher than that in conventional die castings at various pouring temperatures. There exists a critical value for pouring temperature, which is closely related to die temperature and releasing agent. The desirable pouring temperature is 700 ℃ under the SSS condition, and the dendrite primary α-Al phase can be observed in the alloy at the pouring temperature. Compared with that in the alloy poured at higher temperature, the primary and secondary dendritic arm becomes shorter in the alloy, exhibiting better tensile properties.

关 键 词：铝合金 超低速 压铸 浇注温度 力学性能 微观组织 

分 类 号：TG249.2[金属学及工艺—铸造] TG146.21[一般工业技术—材料科学与工程]