铝含量对SPHC镇静钢板再结晶γ纤维织构的影响  

Effect of Al Content on Recrystallized γ Fiber Texture for SPHC Killed Steel Sheet

作　　者：姚无病[1] 胡恒法[1] 赵骧[2] 

机构地区：[1]上海梅山钢铁股份有限公司技术中心,江苏南京210037 [2]东北大学材料各向异性与织构教育部重点实验室,辽宁沈阳110004

出　　处：《物理测试》2008年第4期26-29,共4页Physics Examination and Testing

摘　　要：借助于X射线衍射的三维取向分布函数(ODF)分析,研究了铝含量对SPHC镇静钢板样品的再结晶γ纤维织构的影响。结果表明:γ纤维织构的强度随着铝含量的增加而增强,当Al含量增加到0.037%时γ纤维织构的强度显著增强。这是由于Al与N结合形成的AlN原子集团对再结晶{111}织构的阻碍作用明显小于对{100}织构阻碍作用所致。The effect of Al content on recrystallized γ fiber texture of SPHC killed steel sheet were investigated by the X-ray diffraction ODF analysis. The result showed that intensity of the γ fiber texture is increased with the increase of the Al content. When Al content is 0. 037 %, the intensity of the recrystallized γ fiber texture is the highest. The possible reason is that hindrance of AlN to {111} texture is weaker than that to {100}.

关 键 词：SPHC 退火 再结晶γ纤维织构 铝含量 

分 类 号：TG111.7[金属学及工艺—物理冶金]