Effect of doping elements on catalytic performance of CeO_2-ZrO_2 solid solutions  

作　　者：李梅 柳召刚 胡艳宏 王觅堂 励杭泉 

机构地区：[1]School of Materials Science and Engineering, Beijing University of Chemical Engineering [2]School of Materials and Metallurgy, Inter Mongolia University of Science and Technology

出　　处：《Journal of Rare Earths》2008年第3期357-361,共5页稀土学报（英文版）

基　　金：the National Key Basic Research Program (NKBRP 20047CCA03900);the National Natural Science Foundation of China (50662002)

摘　　要：CeZr, CeYZr, LaCeZr, LaCePrZr, LaCePrYZr, and LaCePr solid solutions were prepared via the coprecipitation method, and characterized by means of X-Ray Diffraction （XRD） and Brunauer-Emmett-Teller （BET） techniques. The oxygen storage capacity （OSC） of the solid solutions was evaluated by the pulse technique and the catalytic activity was assessed using a 4-channel catalysis device. It was seen that the solid solutions presented cubic structure. The specific surface area and thermal stability could be enhanced by doping Y into the solid solutions. Doping a small amount of La had a positive effect on the thermal durability while doping a large amount of La decreased the specific surface area and the thermal stability. LaCePrZr and LaCePrYZr solid solutions synthesized using Baotou rare earth mineral residue enriched with LaCePr after Nd extraction presented a certain higher value in specific surface area and thermal stability, thereby enabling to be used as economic catalysts for automobile exhaust purification. Coating Al2O3 or SiO2 layer on the surface of ceria-zirconia solid solutions increased the specific surface area and thermal resistance.CeZr, CeYZr, LaCeZr, LaCePrZr, LaCePrYZr, and LaCePr solid solutions were prepared via the coprecipitation method, and characterized by means of X-Ray Diffraction （XRD） and Brunauer-Emmett-Teller （BET） techniques. The oxygen storage capacity （OSC） of the solid solutions was evaluated by the pulse technique and the catalytic activity was assessed using a 4-channel catalysis device. It was seen that the solid solutions presented cubic structure. The specific surface area and thermal stability could be enhanced by doping Y into the solid solutions. Doping a small amount of La had a positive effect on the thermal durability while doping a large amount of La decreased the specific surface area and the thermal stability. LaCePrZr and LaCePrYZr solid solutions synthesized using Baotou rare earth mineral residue enriched with LaCePr after Nd extraction presented a certain higher value in specific surface area and thermal stability, thereby enabling to be used as economic catalysts for automobile exhaust purification. Coating Al2O3 or SiO2 layer on the surface of ceria-zirconia solid solutions increased the specific surface area and thermal resistance.

关 键 词：ceria-zirconia solid solutions oxygen storage materials rare earth doped catalysts 