聚羧酸MAA-1室温潮态交联免烫整理工艺的研究  

Study on the moisture crosslinking of cotton fabrics with polycarboxylic acid (MAA-1) at room temperature

作　　者：田鹏[1] 黄玲[1] 

机构地区：[1]陕西科技大学,陕西西安710021

出　　处：《印染助剂》2008年第8期39-41,共3页Textile Auxiliaries

基　　金：陕西省自然科学基础研究计划项目2006B24

摘　　要：在室温条件下,采用自制聚羧酸对棉织物进行潮态交联,通过对整理剂用量、含潮率、堆置时间和催化剂用量的研究,并与干态交联进行对比,确定了最佳工艺:二浸二轧(轧余率80%,聚羧酸MAA-1 90 g/L,催化剂次磷酸钠50 g/L,pH=2.0),含潮率8%,密封堆置16 h,织物的折皱回复角在230°左右.Selfmade polycarboxylic acid was used as cotton moisture crosslinking agent at room temperature. According to studies on finishing agent dosage, moisture regain, stack time, catalyst dosage and compared with that of dry crosslinking, the optimal technique was obtained： 2 dips 2 nips（mangle expression was 80%, polycarboxylic acid MAA-1 90 g/L, catalyst sodium hypophosphite 50 g/L, pH=2.0）, moisture retention was 8%, hermetically stacked for 16 h, and the wrinkle recovery angle of the finished fabrics was about 230°.

关 键 词：聚羧酸MAA-1 潮态交联 免烫 