White organic light-emitting device with both phosphorescent and fluorescent emissive layers  

作　　者：张丽娟 华玉林 吴小明 王宇 印寿根 

机构地区：[1]Key Laboratory of Display Materials and Photoelectric Devices, Ministry of Education [2]Key Laboratory of Photoelectric Materials and Devices of Tianjin, Institute of Material Physics, Tianjin University of Technology

出　　处：《Chinese Physics B》2008年第8期3097-3102,共6页中国物理B（英文版）

摘　　要：This paper reports the fabrication of novel white organic light-emitting device（WOLED） by using a high efficiency blue fluorescent dye N-（4-（（E）-2-（6-（（E）-4-（diphenylamino）styryl）naphthalen-2-yl）vinyl）phenyl）oN- phenylbenzenamine （N-BDAVBi） and a red phosphoresecent dye bis （1-（phenyl） isoquinoline） iridium （III） acetylanetonate （Ir（piq）2（acac））. The configuration of the device was ITO/PVK：TPD/CBP： N-BDAVBi /CBP/ BALq： Ir（piq）2（acac）/BCP/Alq3/LiF：AL. By adjusting the proportion of the dopants （N-BDAVBi, Ir（piq）2（acac）） in the light-emitting layer, white light with Commission Internationale de l＇Eclairage （CIE） coordinates of （0.35, 0.35） and a maximum luminance of 25350cd/m2 were obtained external quantum and current efficiency of 6.78% and between the two light-emitting layers and using BCP at an applied voltage of 22V. The WOLED exhibits maximum 12cd/A respectively. By placing an undoped spacer CBP layer as hole blocking layer, the colour stabilization slightly changed when the driving voltage increased from 6 to 22 V.This paper reports the fabrication of novel white organic light-emitting device（WOLED） by using a high efficiency blue fluorescent dye N-（4-（（E）-2-（6-（（E）-4-（diphenylamino）styryl）naphthalen-2-yl）vinyl）phenyl）oN- phenylbenzenamine （N-BDAVBi） and a red phosphoresecent dye bis （1-（phenyl） isoquinoline） iridium （III） acetylanetonate （Ir（piq）2（acac））. The configuration of the device was ITO/PVK：TPD/CBP： N-BDAVBi /CBP/ BALq： Ir（piq）2（acac）/BCP/Alq3/LiF：AL. By adjusting the proportion of the dopants （N-BDAVBi, Ir（piq）2（acac）） in the light-emitting layer, white light with Commission Internationale de l＇Eclairage （CIE） coordinates of （0.35, 0.35） and a maximum luminance of 25350cd/m2 were obtained external quantum and current efficiency of 6.78% and between the two light-emitting layers and using BCP at an applied voltage of 22V. The WOLED exhibits maximum 12cd/A respectively. By placing an undoped spacer CBP layer as hole blocking layer, the colour stabilization slightly changed when the driving voltage increased from 6 to 22 V.

关 键 词：WOLED colour stability N-BDAVBi 

分 类 号：TN383[电子电信—物理电子学]