Preparation of Al/Si functionally graded materials using ultrasonic separation method  

作　　者：Zhang Zhongtao Li Tingju Yue Hongyun Zhang Jian Li Jie 

机构地区：[1]School of Materials Science and Engineering, Dalian University of Technology, Dalian 116023, China [2]State Key Laboratory of Materials Modification by Laser, Ion and Electron Beams, Dalian University of Technology, Dalian 116023, China

出　　处：《China Foundry》2008年第3期194-198,共5页中国铸造（英文版）

基　　金：the National Natural Science Foundation of China(No.50474055)

摘　　要：Functionally graded materials （FGM） have been widely used in many industries such as aerospace, energy and electronics. In this experimental study of fabricating FGM, an approach was developed to prepare AI/Si FGM using power ultrasonic separation method. Material sample with continuously changing composition and performance/properties was successfully produced. Results showed that the microstructure of the FGM sample transited, from its top to bottom, from the hypereutectic structure with a large quantity of primary Si gradually to the eutectic, and finally to the hypoeutectic with numerous primary AI dendrites. The distribution of primary Si and microhardness of the FGM sample also presented graded characteristics, resulting that the wear resistance of the FGM sample decreased from top to bottom. Preliminary discussion was made on the mechanism of the formation of AI/Si FGM.Functionally graded materials(FGM)have been widely used in many industries such as aerospace, energy and electronics.In this experimental study of fabricating FGM,an approach was developed to prepare Al/Si FGM using power ultrasonic separation method.Material sample with continuously changing composition and performance/properties was successfully produced.Results showed that the microstructure of the FGM sample transited,from its top to bottom,from the hypereutectic structure with a large quantity of primary Si gradually to the eutectic,and finally to the hypoeutectic with numerous primary Al dendrites.The distribution of primary Si and microhardness of the FGM sample also presented graded characteristics,resulting that the wear resistance of the FGM sample decreased from top to bottom.Preliminary discussion was made on the mechanism of the formation of Al/Si FGM.

关 键 词：functionally graded materials （FGM） aluminum alloys ultrasonic cavitation acoustic streaming DEGASSING 

分 类 号：TG146.21[一般工业技术—材料科学与工程]