丙烯酸甲酯接枝亚麻纤维及其在PVC／亚麻复合材料中的应用  

Graft of methyl acrylate on flax fiber and its application in PVC/flax composites

作　　者：韩志超[1] 迟红训[2] 王少廷[1] 左勇[1] 刘俊龙[1] 

机构地区：[1]大连工业大学化工与材料学院,辽宁大连116034 [2]辽东学院基础部,辽宁丹东118003

出　　处：《大连工业大学学报》2008年第3期241-244,共4页Journal of Dalian Polytechnic University

摘　　要：以过硫酸钾(K2S2O8)为引发剂,制备了Flax-g-MA接枝物。研究了反应条件对接枝率和接枝效率的影响。结果表明,接枝率和接枝效率均随着单体用量的增加而增大,随引发剂用量的增加和反应温度的升高先增大后减小,随反应时间的延长而逐渐增大并趋于平衡。当反应温度为60℃,反应时间为4 h,引发剂与单体质量比为0.12,单体与亚麻质量比为1.2时,接枝率和接枝效率最高。加入MA单体接枝改性的亚麻纤维后,有效地改善了PVC/亚麻复合材料的各项性能。Flax-g-MA was prepared by using potassium persulfate as initiator. The result showed that the grafting degree and grafting efficiency was increased with the increase of monomer amount, and increased at first and then decreased with the increase of initiator amount and the reaction temperature. Maximum grafting rate and grafting efficiency were obtained at θ= 60 ℃, t = 4 h, rn（K2 S2 O8 ）/m （MA）=0.12, m（MA）/m（flax）= 1.2. The mechanical properties of the composites were improved significantly by adding flax-g-MA.

关 键 词：亚麻纤维 PVC树脂 丙烯酸甲酯 接枝 

分 类 号：TQ327[化学工程—合成树脂塑料工业] TS102.221[轻工技术与工程—纺织工程]