熔盐法制备Bi_4Ti_3O_(12)粉体显微形貌的研究  

Study on micromorphology of Bi_4Ti_3O_(12) powder prepared by molten salt method

作　　者：宁青菊[1] 李艳杰[1] 武利娜[1] 

机构地区：[1]陕西科技大学材料科学与工程学院,陕西西安710021

出　　处：《电子元件与材料》2008年第10期54-57,共4页Electronic Components And Materials

基　　金：国家自然科学基金资助项目(No.50607013)

摘　　要：采用熔盐法制备了晶粒取向生长的Bi4Ti3O12粉体。研究了煅烧温度以及盐与原料的质量比等因素对粉体显微形貌的影响。结果表明:随着煅烧温度的升高,晶粒尺寸增大,分散性变好,a-b面内取向生长明显。当盐与原料质量比为1:1,900℃煅烧2h后得到的粉体显微形貌较好,晶粒呈规则的四边形薄片状,尺寸分布均匀,平均粒径约7μm。Bi4Ti3O12 powders with grain oriented growth were prepared by molten salt method. The effects of calcining temperature and mass ratio of salt to raw materials on the micromorphology ofBi4Ti3O12 powders were investigated. The results show that an increase of the grain size, better dispersivity and significant oriented growth in a-b plane occur with increasing calcining temperature. Bi4Ti3O12 powders with good micromorphologies are obtained when mass ratio of salt to raw materials is 1：1, calcining at 900℃ for 2 h. The grain is regular quadrilateral flake-like and homogenous distributed. The average particle size is about 7μm.

关 键 词：无机非金属材料 BI4TI3O12 熔盐法 显微形貌 无铅铁电压电陶瓷 

分 类 号：TN384[电子电信—物理电子学] O782.4[理学—晶体学]