Physical dispersion state and fluorescent property of Eu-complex in the Eu-complex/silicon rubber composites  

作　　者：温世鹏 胡水 张小萍 张立群 刘力 

机构地区：[1]Key Laboratory of Beijing City on Preparation and Processing of Novel Polymer Materials, Beijing University of Chemical Technology [2]Key Laboratory for Nanomaterials, Ministry of Education, Beijing University of Chemical Technology

出　　处：《Journal of Rare Earths》2008年第5期626-632,共7页稀土学报（英文版）

基　　金：the National Natural Science Foundation of China,the China Energy Conservation Investment Corporation (50173004 and 50503002);the Beijing New Star Project (2003A11);the National High-Tech. Research Developing Foundation (863,2003AA324030);Beijing Municipal Commission of Education (JD100100403);National Key Project of Scientific and Technical Supporting Programs Funded by Ministry of Science & Technology of China (2006BAE03B)

摘　　要：The fluorescent complex Eu（TTA）2（Phen）（MA） （HTTA=2-Thenoyltrifluoroacetone, Phen=1,10-phenanthroline, MA=Maleic an- hydrider） was synthesized and characterized with elemental analysis, infrared spectrum （IR）, scanning electron microscope （SEM）, X-ray Diffraction（XRD）, differential scanning calorimetry（DSC）, and fluorescent measurement. To explore the effect of different physical dispersion state of Eu-complex on the fluorescent property of the Eu-complex/silicon rubber composites, various quantifies of Eu（TTA）2（phen） （MA） were mixed with silicon rubber （SIR） and peroxide to form uncured composites. These composites were vulcanized to obtain cured Eu-complex/SiR composites at 250 ℃, which was higher than the melting-point of Eu-complex. The SEM, XRD, DSC, and the fluorescent measurement of these composites showed that both the complex molecules dispersed in the silicon rubber during the melting process and the parent Eu-complex particles had positive effects on fluorescent property, whereas the re-crystallized Eu-complex particles and the aggregating complexes formed during the melting-process had negative effects on fluorescent property. For the uncured composites, their fluorescent intensities almost did not change with the increasing amount of Eu-complex. Furthermore, for the composites with small content of Eu-complex, their fluorescent intensities decreased significantly after curing, and this difference in fluorescent intensity became smaller as the content of Eu-complex increases.The fluorescent complex Eu（TTA）2（Phen）（MA） （HTTA=2-Thenoyltrifluoroacetone, Phen=1,10-phenanthroline, MA=Maleic an- hydrider） was synthesized and characterized with elemental analysis, infrared spectrum （IR）, scanning electron microscope （SEM）, X-ray Diffraction（XRD）, differential scanning calorimetry（DSC）, and fluorescent measurement. To explore the effect of different physical dispersion state of Eu-complex on the fluorescent property of the Eu-complex/silicon rubber composites, various quantifies of Eu（TTA）2（phen） （MA） were mixed with silicon rubber （SIR） and peroxide to form uncured composites. These composites were vulcanized to obtain cured Eu-complex/SiR composites at 250 ℃, which was higher than the melting-point of Eu-complex. The SEM, XRD, DSC, and the fluorescent measurement of these composites showed that both the complex molecules dispersed in the silicon rubber during the melting process and the parent Eu-complex particles had positive effects on fluorescent property, whereas the re-crystallized Eu-complex particles and the aggregating complexes formed during the melting-process had negative effects on fluorescent property. For the uncured composites, their fluorescent intensities almost did not change with the increasing amount of Eu-complex. Furthermore, for the composites with small content of Eu-complex, their fluorescent intensities decreased significantly after curing, and this difference in fluorescent intensity became smaller as the content of Eu-complex increases.

关 键 词：polymer-matrix composites melting blending physical dispersion state fluorescent property rare earths 

分 类 号：TB332[一般工业技术—材料科学与工程]