Al-Zr-Cr-La合金中多元弥散相的形成及其强化作用  

Formation and Effects of Al-Zr-Cr-La Dispersoid in Aluminum Alloy

作　　者：陈康华[1] 周年润[1] 方华婵[1] 陈祥[1] 

机构地区：[1]中南大学粉末冶金国家重点实验室

出　　处：《特种铸造及有色合金》2008年第10期788-791,共4页Special Casting & Nonferrous Alloys

基　　金：国家重点基础研究发展计划(973计划)资助项目(2005CB623704);国家自然基金委创新研究群体科学基金资助项目(50721003);国家自然科学基金资助项目(50471057);国防重点实验室基金资助项目

摘　　要：研究了Al-Zr-Cr-La合金中多元弥散相的形成及其对合金的强化作用。结果表明,在合金中形成具有Al20Cr2La结构的弥散相;在含Zr的合金中,Zr溶入到Al20Cr2La相中。这种结构的弥散相,具有明显的抑制再结晶和强化合金效果。相对于无Zr的Al20Cr2La相,含Zr的Al20Cr2La相抑制再结晶能力尤为显著,强化合金能力也略有提高。Formation and effects of Al-Zr-Cr-La dispersoid in aluminum alloy were investigated. The results show that Al20Cr2La dispersoids are created in the alloy, which can evidently restrain the recrystalization and enhance the alloy, and Zr element can be dissolved into the Al20Cr2La phase in the alloy containing Zr. Compared with the Al20Cr2La phase without Zr, the Al20Cr2La phase with Zr exhibits higher capability of inhibiting recrystalization with slight improvement of enhancing alloy.

关 键 词：Al-Zr-Cr-La合金 Al20Cr2La 弥散相 再结晶 强化 

分 类 号：TG146.21[一般工业技术—材料科学与工程]