Preparation of NH_4ZrH(PO_4)_2·H_2O via solid-state reaction at low heat and its catalytic performance in the synthesis of butyl acetate  

作　　者：WU Wenwei LAI Shuibin WU Xuehang LIAO Sen HOU Shengyi 

机构地区：[1]School of Chemistry and Chemical Engineering, Guangxi University, Nanning 530004, China

出　　处：《Rare Metals》2008年第5期550-554,共5页稀有金属（英文版）

基　　金：the Natural Science Foundation of Guangxi Province, China (No. 0640009)

摘　　要：Nanocrystalline NH4ZrH（PO4）2·H2O was obtained by grinding ZrOC12·8H2O and （NH4）2HPO4 in the presence of surfactant PEG-400 via solid-state reaction at room temperature. The product NH4ZrH（PO4）2·H2O and its product of thermal decomposition were characterized using thermogravimetry and differential thermal analyses （TG/DTA）, Fourier transform infrared spectroscopy （FT-IR）, X-ray powder diffraction （XRD）, and transmission electron microscopy （TEM）. Nanocrystalline NHaZrH（PO4）2·H2O with an average particle size of 17 nm was obtained when the product was kept at80℃ for 3 h. Its crystalline framework was stable at temperatures below 250℃. In addition, the catalytic performance of NH4ZrH（PO4）2·H2O in the synthesis of butyl acetate was investigated. The results show that NH4ZrH（PO4）2·H2O behaved as an excellent heterogeneous catalyst in the synthesis of butyl acetate.Nanocrystalline NH4ZrH（PO4）2·H2O was obtained by grinding ZrOC12·8H2O and （NH4）2HPO4 in the presence of surfactant PEG-400 via solid-state reaction at room temperature. The product NH4ZrH（PO4）2·H2O and its product of thermal decomposition were characterized using thermogravimetry and differential thermal analyses （TG/DTA）, Fourier transform infrared spectroscopy （FT-IR）, X-ray powder diffraction （XRD）, and transmission electron microscopy （TEM）. Nanocrystalline NHaZrH（PO4）2·H2O with an average particle size of 17 nm was obtained when the product was kept at80℃ for 3 h. Its crystalline framework was stable at temperatures below 250℃. In addition, the catalytic performance of NH4ZrH（PO4）2·H2O in the synthesis of butyl acetate was investigated. The results show that NH4ZrH（PO4）2·H2O behaved as an excellent heterogeneous catalyst in the synthesis of butyl acetate.

关 键 词：NANOCRYSTALLINE solid-state reaction butyl acetate CATALYSIS 