MMA熔融接枝POE的研究  

Study on MMA melt grafting POE

作　　者：李海兰[1] 王卫卫[1] 邱桂学[1] 

机构地区：[1]青岛科技大学,山东青岛266042

出　　处：《弹性体》2008年第5期15-18,共4页China Elastomerics

摘　　要：利用熔融接枝法制备了甲基丙烯酸甲酯(MMA)接枝乙烯-辛烯共聚物(POE-g-MMA),探讨了各种因素对POE-g-MMA接枝率和熔体流动速率(MFR)的影响,得出了最佳配方——MMA:1.75 g/(50 gPOE),DCP:0.25 g/(50 gPOE),第二单体苯乙烯(St)的加入使接枝率有所提高,St与MMA的量比为1,接枝率达到最高;最佳工艺条件:温度为150℃,反应时间为10 min,螺杆转速为80 r/min。Methyl methacrylate （MMA） grafted ethylene-oetene copolymer （POE-g-MMA） was prepared by melt-grafting. The infuences on the graft ratio of POE-g-MMA and MFR were studied, and the optimum contents of MMA and dieumyl peroxide DCP were determined to be 1. 75 g/（50 gPOE）, 0.25 g/（50 gPOE） respectively. When St/MMA is 1 （mol mass）,the graft ratio is the grea test. The best technical conditions are as follows：temperature is 150℃,screw speed is 80 r/min^-1,re active time is 10 min.

关 键 词：乙烯-辛烯其聚物(POE) 甲基丙烯酸甲酯 苯乙烯 接枝率 熔体流动速率 