PVC热稳定剂的微胶囊化工艺研究  

Study on the microcapsulization technics of PVC heat stabilizers

作　　者：童晓梅[1] 张敏[1] 张婷[1] 陈峰[1] 李猛[1] 

机构地区：[1]陕西科技大学化学与化工学院,西安710021

出　　处：《化工新型材料》2008年第11期46-48,共3页New Chemical Materials

摘　　要：以PVC为囊壁材料,水滑石、钙/锌复合热稳定剂为囊芯材料,制备了高效、环保的PVC复合热稳定剂微胶囊,并探讨了该微胶囊的最佳制备工艺。结果表明,所制备的微胶囊固含量为15%,当搅拌速度为600r/min,搅拌时间为160min,溶剂四氢呋喃与非溶剂乙二醇的比为5∶3,乳化剂Span80的量为3%,所得微胶囊结构紧密、粒径分布100~450μm。该热稳定剂微胶囊具有一定的应用前景。High Efficient, environment friendly PVC heat stabilizers were prepared by microcapsulation technology using PVC as wall material, water talc and calcium / zinc compound heat stabilizers as core materials. The PVC heat stabilizers＇ best microcapsulization technics were discussed. The results showed that the solid content of the microcapsules was 15% , when the mixing speed was 600r/min, stirring time was 160min, the ratio of solvent tetrahydrofuran to non-solvent glycol was 5 ： 3, the amount of emulsifier Span80 was 3%. Microcapsules with close structure, size distribution 100- 450um were obtained. The mierocapsulation of heat stabilizers had certain application prospect.

关 键 词：PVC 热稳定剂 微胶囊 水滑石 钙/锌复合热稳定剂 

分 类 号：TQ325.3[化学工程—合成树脂塑料工业]