Fabrication of Poly(4-vinylpyridine) Nanofiber and Fluorescent Poly(4-vinylpyridine)/Porphyrin Nanofiber by Electrospinning  

作　　者：SONG Yan ZHAN Nai-qian YU Miao YANG Qing-biao ZHANG Chao-qun WANG Heng-guo LI Yao-xian 

机构地区：[1]College of Chemistry, Jilin University, Changehun 130021, P. R. China [2]School of Chemical and Material Engineering, Jilin Institute of Chemical Teehology, Jilin 132022, P R. China

出　　处：《Chemical Research in Chinese Universities》2008年第6期722-725,共4页高等学校化学研究（英文版）

基　　金：Supported by the National Natural Science Foundation of China(No.20674023)

摘　　要：Poly（4-vinylpyridine）（P4-VP） nanofiber and fluoresent poly（4-vinylpyridine）/porphyrin（P4-VP/TPPA） nanofiber were respectively prepared by electrospinning. The effect of the concentration of P4-VP/dimethylformamide （DMF） electrospinning solutions on the morphology of P4-VP nanofiber was investigated and it was found that the average diameter of the nanofiber of P4-VP/DMF increased with the increase of the concentration of the spinning solution. After the addition of TPPA to the P4-VP/DMF spinning solution, the diameter of P4-VP/TPPA nanofiber became even due to the increase of the conductivity of the P4-VP/DMF-TPPA solution. The photoluminescent（PL） spectral analysis indicates that the emission peak position of P4-VP/TPPA nanofiber is almost the same as that of pure TPPA at about 650 nm without peak shift, and when it was stored for 20 days, the emission peak of P4-VP/TPPA nanofiber is also at 650 nm, indicating that the fluorescent property of P4-VP/TPPA nanofiber is stable. Fourier-transform iufrared（FTIR） spectrum confirms the chemical composition of the resulting P4-VP/TPPA composite nanofiber.Poly（4-vinylpyridine）（P4-VP） nanofiber and fluoresent poly（4-vinylpyridine）/porphyrin（P4-VP/TPPA） nanofiber were respectively prepared by electrospinning. The effect of the concentration of P4-VP/dimethylformamide （DMF） electrospinning solutions on the morphology of P4-VP nanofiber was investigated and it was found that the average diameter of the nanofiber of P4-VP/DMF increased with the increase of the concentration of the spinning solution. After the addition of TPPA to the P4-VP/DMF spinning solution, the diameter of P4-VP/TPPA nanofiber became even due to the increase of the conductivity of the P4-VP/DMF-TPPA solution. The photoluminescent（PL） spectral analysis indicates that the emission peak position of P4-VP/TPPA nanofiber is almost the same as that of pure TPPA at about 650 nm without peak shift, and when it was stored for 20 days, the emission peak of P4-VP/TPPA nanofiber is also at 650 nm, indicating that the fluorescent property of P4-VP/TPPA nanofiber is stable. Fourier-transform iufrared（FTIR） spectrum confirms the chemical composition of the resulting P4-VP/TPPA composite nanofiber.

关 键 词：Poly（4-vinylpyridine） PORPHYRIN NANOFIBER ELECTROSPINNING 

分 类 号：O63[理学—高分子化学]