Study on Toughening Epoxy Resin by Using CTBN Rubber

作　　者：姚兴芳[1] 张世锋[2] 

机构地区：[1]天津城市建设学院材料科学与工程系,天津300384 [2]北京林业大学材料与技术学院,北京100083

出　　处：《化学与粘合》2008年第6期13-15,共3页Chemistry and Adhesion

基　　金：建设部项目"耐高温建筑结构胶的研制及应用"(编号:03-2-019)

摘　　要：制备了由端羧基液体丁腈橡胶(CTBN)增韧环氧树脂(ER)于室温下固化的双组分胶黏剂。研究了CTBN与ER配比、甲组分处理温度及其保温时间对胶黏剂剪切强度的影响并用扫描电子显微镜(SEM)观察了其微观形态。实验结果表明CTBN∶ER=8∶1、甲组分于200℃下反应2.5h时,胶黏剂剪切强度可以达到25.34MPa,耐介质性能良好。同时SEM测试结果表明端羧基液体丁腈橡胶对ER增韧作用明显,为提高环氧树脂的粘接性和韧性提供了技术依据。The two- component epoxy resin （ER） adhesive toughened by using liquid carboxyl terminated butadiene nitrile rubber （CTBN） was prepared. The influences of the ratio of CTBN： ER, reaction temperature and time for the first ingredient on shearing strength of the adhesives were studied in detail. And scanning electron microscope （SEM） was used to observe the product＇s micro morphology. The results show that when CTBN： ER = 8：1 and the first ingredient reacts at 200℃ for 2.5h, the shearing strength of the adhesive reaches 25.34MPa and its medium - resistance is exeellent. The SEM result indicates that CTBN has remarkably toughed ER.

关 键 词：端羧基液体丁腈橡胶 环氧树脂 胶黏剂 剪切强度 

分 类 号：TQ433.437[化学工程]