复合催化剂催化D,L-丙交酯的合成实验研究  

Study on the Catalytic Synthesis of D,L-lactide with Composite Catalyst

作　　者：冯辉霞[1] 赵丹[1] 张建强[1] 张苗[1] 陈娜丽[1] 

机构地区：[1]兰州理工大学石油化工学院,甘肃兰州730050

出　　处：《化学与粘合》2008年第6期32-35,共4页Chemistry and Adhesion

基　　金：甘肃省自然科学基金资助项目(编号:3ZS062-B25-027;3ZS-042-B25-008)

摘　　要：D，L-丙交酯（DLLA）是合成聚乳酸的关键中间体，其收率直接影响到聚乳酸的收率。采用氯化亚锡／氧化锌做为复合催化剂，研究合成丙交酯的反应条件，提高了丙交酯的收率。实验结果表明：当采用复合催化剂，氯化亚锡：氧化锌的质量比=4：1，其用量为乳酸质量的1％，在减压条件下（20kPa），130—140℃脱水3．5h，馏出温度为220℃时，可使DLLA收率最大为36．0％。The key intermediate for synthesizing poly - lactic acid （PLA） is D, L - lactide （ DLLA ）. The yield of D, L - lactide influences that of PLA directly. The reaction conditions for synthesizing DLLA were studied with using SnCl2/ZnO as composite catalyst, and the yield of DLLA was improved. The results show that the yield of D, L - lactide reaches 36% when using SnCl2/ZnO =4：1 as catalyst, and its amount content is 1% （ based on total mass of reactants）, at low pressure （20kPa）, the dehydration time is 3.5h at 130 - 140℃ and the distillation temperature is 220℃.

关 键 词：D L-丙交酯(DLLA) 聚乳酸 氯化亚锡/氧化锌 合成 馏出温度 

分 类 号：TQ426.94[化学工程]