The Synthesis Technique of Polyacrylic Acid Superplasticizer  

作　　者：张荣国 雷家珩 

机构地区：[1]School of Science,Wuhan University of Technology

出　　处：《Journal of Wuhan University of Technology(Materials Science)》2008年第6期830-833,共4页武汉理工大学学报（材料科学英文版）

基　　金：Funded by the Research Item from Ministry of Communications Tech-nology Project(No. 2007319811130)

摘　　要：Using water separation technique,acrylic acid （AA） and polyethylene glycol （PEG） 1000,of which the ratio was 1.5,were esterified and the optimum esterification ratio of 90% could be reached under the condition of 110 ℃×3 h.Using polyoxyethylene acrylate macromonomer （PA） prepared in the esterification,AA and sodium methylacryl sulfonate （MAS） as monomers,a copolymer which could be used as superplasticizer was prepared by free radical coolymerization in n（PA）：n（AA）：n（MAS） of 1：7：3.When the synthesis condition was 80 ℃× 5 h,the optimal dosage of initiator was 3.0%-4.0%,the fluidity of cement paste with the samples could reach 270 mm.By analyzing the effect of the content of residual small molecule sulfonic monomer on the properties of sample,n（MAS）/n（PA） was controlled in a range of 2.5-3.8.Using water separation technique,acrylic acid （AA） and polyethylene glycol （PEG） 1000,of which the ratio was 1.5,were esterified and the optimum esterification ratio of 90% could be reached under the condition of 110 ℃×3 h.Using polyoxyethylene acrylate macromonomer （PA） prepared in the esterification,AA and sodium methylacryl sulfonate （MAS） as monomers,a copolymer which could be used as superplasticizer was prepared by free radical coolymerization in n（PA）：n（AA）：n（MAS） of 1：7：3.When the synthesis condition was 80 ℃× 5 h,the optimal dosage of initiator was 3.0%-4.0%,the fluidity of cement paste with the samples could reach 270 mm.By analyzing the effect of the content of residual small molecule sulfonic monomer on the properties of sample,n（MAS）/n（PA） was controlled in a range of 2.5-3.8.

关 键 词：polyacrylic acid SUPERPLASTICIZER ESTERIFICATION free radical polymerization 

分 类 号：TQ320.6[化学工程—合成树脂塑料工业]