La_(0.6)Ce_xNd_(0.4-x)Ni_(3.0)Co_(0.2)Al_(0.3)(x=0～0.4)合金储氢性能研究  

Study on the Hydrogen Storage Characteristics of La_(0.6)Ce_xNd_(0.4-x)Ni_(3.0)Co_(0.2)Al_(0.3)(x=0～0.4) Alloys

作　　者：刘淑辉[1] 蒋龙[1] 栾天阳[1] 黎光旭[1] 韦文楼[1] 郭进[1] 

机构地区：[1]广西大学物理科学与工程技术学院,广西南宁530004

出　　处：《广西科学》2008年第4期404-407,共4页Guangxi Sciences

基　　金：国家自然科学基金项目(50561002);广西科学基金项目(桂科自0728028);广西大学科研重点项目(2004ZD04);广西教育厅科研(桂教科研[2006]26-8);广西大学硕士研究生科研创新项目资助

摘　　要：采用电弧炉熔炼方法制备La0.6CexNd0.4-xNi3.0Co0.2Al0.3(x=0～0.4)系列合金,并对合金的储氢性能和电化学性能进行测试。测试结果表明,合金在Ce=0时具有最高的电化学容量(284.2mAh/g)和储氢量(0.93wt%)。Ce的添加会降低合金放电容量,但是能够改善合金的循环稳定性能。La0.6CexNd0.4-xNi3.0Co0.2Al0.3（X=0～0.4） hydrogen storage alloys were prepared by induction melting, the hydrogen storage and electrochemical properties of the alloys were measured and analyzed in detail. The results show that La0.6Nd0.4Ni3.0Co0.2Al0.3 alloy has better hydrogen storage capacity and higher electrochemical properties. The addition of Ce can decrease the discharge capacity but enhance the cycling stabilities.

关 键 词：合金 储氢性能 热力学参数 