阻燃涤纶/棉织物的阻燃整理  

Flame-retardant finish of flame-retardant polyester/cotton fabric

作　　者：王晓春[1] 傅裕[2] 

机构地区：[1]北京服装学院材料研究开发与评价重点实验室,北京100029 [2]北京服装学院材料科学与工程学院,北京100029

出　　处：《印染》2009年第1期10-12,26,共4页China Dyeing and Finishing

基　　金：北京市重点实验室开放课题(2006ZK-4)

摘　　要：采用棉用阻燃剂FPK8002对阻燃涤纶/棉织物进行阻燃整理,探讨阻燃剂浓度、焙烘条件及交联剂用量对织物阻燃性能的影响,分析阻燃涤纶含量和织物组织结构对阻燃涤纶/棉织物阻燃性能的影响。阻燃涤纶/棉织物阻燃整理的优化工艺为阻燃剂FPK8002用量350g/L,交联剂用量350g/L,焙烘温度160℃,焙烘时间4min。测试结果表明,整理织物的裂解温度明显降低,阻燃性能符合国家B1级标准。Flame-retardant finish was carried out on flame-retardant polyester/cotton fabric with tlame-retaroant agent FPK8002 Influences of concentration of flame-retardant agent, curing conditions, dosage of crosslinking agent, content of flame-retardant polyester and fabric construction on flame retardancy were studied. The optimized flame-retardant cond tons were as follows： FPK8002 3.50 g/L, crosslinking agent 350 g/L, and curing at 160 ℃ for 4 min; decomposition temperature of treated fabric dropped obviously, and flame retardancy met B1 grade of national standard.

关 键 词：阻燃整理 阻燃剂 涤棉织物 

分 类 号：TS195.592[轻工技术与工程—纺织化学与染整工程]