镁铁水滑石焙烧产物催化合成乙酸正丁酯  

Synthesis of n-Butyl Acetate with Mixed Oxides as Catalyst Calcined from MgFe-hydrotalcite

作　　者：徐芳[1] 黄婧祎 王仁念[1] 王军涛[1] 

机构地区：[1]咸宁学院化学与生命科学学院,湖北咸宁437100

出　　处：《咸宁学院学报》2008年第6期102-104,共3页Journal of Xianning University

摘　　要：采用低过饱和共沉淀法合成了物质的量比为2,3,4的镁铁水滑石,XRD分析表明它们晶形好,纯度高,以其焙烧产物为催化剂研究了乙酸正丁酯催化合成的各种影响因素.结果表明:3种焙烧产物都可以催化乙酸正丁酯反应,其中2MgFe效果最好,3MgFe次之,4MgFe第三;以2MgFe为催化剂,在最佳合成条件为酸醇摩尔比为1∶2,催化剂用量0.5g,反应时间为2h,催化产率为67.0%.MgFe-Hydrotalcite with Mg/Fe molar ratios of 2 to 4 were synthesized by copreeipitation. All of them had good crystal structures by means of XRD. n-Butyl acetate was synthesized from acetic acid and butanol using mixed oxides catalyst, which were obtained from calcination of MgFe-hydrotalcite. The results showed that all the mixed oxides showed high catalytic, 2 MgFe was the best, 3MgFe was the second,and 4MgFe was the third,the catalytic activity were 67.0% under optimal reaction condition as follows：n（acetic acid） ：n（butanol） = 1：2,catalyst dosage 0.5g,reaction time 2 hour.

关 键 词：镁铁水滑石 焙烧 催化 乙酸正丁酯 