金属波纹膨胀节开裂失效原因分析  

Failure Analysis for Cracking Occurred in Metal Bellow Expansion Joint

作　　者：张玉明[1] 

机构地区：[1]上海市特种设备监督检验技术研究院,上海200062

出　　处：《化工设备与管道》2009年第1期66-68,共3页Process Equipment & Piping

摘　　要：采用宏观检查、扫描电镜、X射线能谱、金相分析及化学分析等方法,对金属波纹膨胀节开裂的原因进行了分析。结果表明应力腐蚀是造成金属波纹膨胀节开裂失效的根本原因,并据此提出了改进建议。By using visual examination, scanning electronic microscope, X - ray energy spectrum and metallurgy and chemical analysis, the cause of crack occurred in bellow expansion joint was analyzed. It has been shown that stress corrosion is the primary cause for inducing the crack occurred in expansion joint. Then, some improvements were proposed.

关 键 词：波纹膨胀节 应力 Cl及S离子 应力腐蚀 马氏体 

分 类 号：TQ050.7[化学工程]