钛酸锶双功能元件固相合成工艺改进的研究  

Study on Improvement of the Solid Phase Synthesis Technique of SrTiO_3 Double Function Component

作　　者：张帅谋[1] 曹全喜[1] 

机构地区：[1]西安电子科技大学技术物理学院,陕西西安710071

出　　处：《压电与声光》2009年第1期136-138,共3页Piezoelectrics & Acoustooptics

基　　金：陕西省攻关基金资助项目(2005k06-G11)

摘　　要：对固相合成法工艺进行了改进。研究了球磨时间与粉料的粒径、均匀度间的关系,发现制备钛酸锶粉料的最佳球磨时间为150 min。通过实验对预焙烧温度参数的优化选择,发现,选择1100℃为预焙烧温度,可改善固相合成法粉料的微观结构及质量,从而可改善压敏-电容双功能元件的电性能。The technique of solid phase synthesis was modified in this paper. The relations between grinding time, grain diameter and degree of homogeneity were also studied. The experimental results showed that the opti- mized ball-milling time of SrTiO3 powder was 150 min. Optimum selection for parameter of pre-sintering tempera- ture was made via experimentation methods. It was found that the microstructure and quality of the powder could be improved when pre-sintering temperature was 1100℃, which could further improved the properties of varistor-capacitance double function components.

关 键 词：钛酸锶 工艺 双功能元件 焙烧温度 

分 类 号：TB323[一般工业技术—材料科学与工程]