热处理条件对喷雾沉积法制备的BiSrCaCuO膜的超导电性的影响  

Influence of Heat-treatment Conditions on the Superconductivity of BiSrCaCuO Films Prepared by Spray Deposition

作　　者：梁路光[1] 曾令文[1] 千正男[1] 吴代鸣[1] 

机构地区：[1]吉林大学物理系

出　　处：《吉林大学自然科学学报》1990年第4期51-53,共3页Acta Scientiarum Naturalium Universitatis Jilinensis

摘　　要：研究了热处理条件对用喷雾沉积法制备BiSCaCuO膜的超导电性的影响。实验表明,膜的超导转变温度对热处理条件是十分灵敏的,最好的热处理条件是:在890℃烧结3 min后迅速降到860℃再恒温30min,然后以10℃/min的速率降至室温。The influence of heat-treatment conditions on the superconductivity of BiSrCaCuO films prepared by spray deposition was investigated. The investigation indicates that the superconducting transition temperature of films is very sensitive to the heat-treatment conditions. The best film with an onset temperature of supercondutivity at around 100 K and zero resistance temperature at 76 K was obtained by annealing at 890 °C for 3 min followed by sintering at 860 °C for 30 min and cooling to room-temperature at a rate of 10 °C/min. X-ray diffraction measurements show that the film is highly textured with the c-axis normal to the suhstrate surface.

关 键 词：膜 超导电性 喷雾沉积法 热处理 

分 类 号：TN304.055[电子电信—物理电子学]