快淬Nd_(3.8)Fe_(74.8)B_(21.4)合金的磁性和结构的研究  

A study on magnetic properties and structure for the Nd 3/8 Fe 74.8 B21/4 alloy

作　　者：金慧娟[1,2] 黄钢祥[1,2] 许桂琴 夏朝珲[1,2] 朱建发 

机构地区：[1]上海钢铁研究所,上海市金属功能材料开发应用重点实验室 [2]上海一钢铸造厂

出　　处：《核技术》1998年第1期39-42,共4页Nuclear Techniques

摘　　要：采用Ｘ射线衍射和穆斯堡尔效应等实验方法研究了快淬Ｎｄ_（３．８）Ｆｅ_（７４．８）Ｂ_（２１．４）合金的磁性和微结构。实验结果表明：经１５ｍ／ｓ辊速快淬得到的非晶条带在６５０℃退火４ｍｉｎ后获得的各向同性细晶粉末具有良好的磁性能。分析还表明此时样品主要由Ｆｅ３Ｂ和Ｎｄ２Ｆｅ１４Ｂ两相组成，另可能有极少量的Ｆｅ２Ｂ相存在，其中软磁相Ｆｅ３Ｂ为主相，约占９０％；而均匀分布于主相的硬磁相Ｎｄ２Ｆｅ１４Ｂ仅占１０％。The magnetic properties and microstructure of the Nd3/8Fe 74/8B21/4 bonded magnethave been investigated in detail by X-ray diffraction and Mossbauer spectroscopyThe samples used for the study were taken from the melt-spun allpy ribbons at 650℃for 4 minhas good magnetic properties.The study on microstructure shows that it consists oftetragonal Fe3B as main phase(about 90% volume fraction)and Nd2Fe14B crystallitephase(less than 10%).In addition, a small amount of Fe2B phase may be present.

关 键 词：快淬永磁材料 磁性能 穆斯堡尔效应 钕铁硼合金 

分 类 号：TG132.27[一般工业技术—材料科学与工程] TG111.92[金属学及工艺—合金]