硫化锌/多孔硅体系和氧化锌/多孔硅体系的光学和电学特性比较  

Comparison of Optical and Electrical Properties of ZnS/Porous Silicon and ZnO/Porous Silicon Systems

作　　者：王彩凤[1] 李清山[2] 胡波[3] 

机构地区：[1]滨州学院物理与电子科学系,山东滨州256603 [2]鲁东大学物理系,山东烟台264025 [3]滨州学院飞行学院,山东滨州256603

出　　处：《液晶与显示》2009年第1期34-37,共4页Chinese Journal of Liquid Crystals and Displays

基　　金：山东省自然科学基金资助项目(No.Y2002A09)

摘　　要：用脉冲激光沉积法在相同孔隙率的多孔硅(Porous Silicon,PS)衬底上生长了ZnS薄膜和ZnO薄膜,在室温下对ZnS/PS和ZnO/PS的光学和电学性质进行了比较。结果发现,ZnS/PS和ZnO/PS在可见光区450～700nm都有一个较宽的光致发光谱带,呈现较强的白光发射,但ZnS/PS体系的白光发射性能要优于ZnO/PS体系的发光性能。从二者的I-V特性曲线来看,ZnS/PS异质结呈现出与普通二极管相似的整流特性,而ZnO/PS异质结的整流特性与普通二极管不同,其反向电流不饱和。ZnS films and ZnO films were prepared on porous silicon （PS） substrates with same porosity by pulsed laser deposition （PLD）, and the optical and electrical properties of ZnS/PS and ZnO/PS sys- tems were compared at room temperature. The results showed that, there was a broad photoluminescenee band from 450 nm to 700 nm in the visible region of both ZnS/PS and ZnO/PS composites, exhibiting intensive white light emission. However, the white light emission performance of ZnS/PS composite was better than that of ZnO/PS composite. Based on the I-V characteristics, ZnS/PS heterojunction exhibited the rectifying junction behavior, but the I-V characteristic of the ZnO/PS heterostructure was different from that of the common diode, whose reverse current was not saturated.

关 键 词：白光发射 光致发光 Ⅰ-Ⅴ特性曲线 硫化锌 氧化锌 多孔硅 

分 类 号：O484.42[理学—固体物理] TN304.12[理学—物理]