Preparation of nano-sized cerium and titanium pyrophosphates via solid-state reaction at room temperature  

作　　者：WU Wenwei FAN Yanjin WU Xuehang LIAO Sen HUANG Xiufu LI Xuanhai 

机构地区：[1]School of Chemistry and Chemical Engineering, Guangxi University, Nanning 530004, China

出　　处：《Rare Metals》2009年第1期33-38,共6页稀有金属（英文版）

基　　金：supported by the Natural Sci-ence Foundation of Guangxi Province, China (No. 0640009)

摘　　要：Nano-sized cerium-titanium pyrophosphates Ce1-xTixP2O7 （with x = 0, 0.2, 0.5, 0.7, 0.9, and 1.0） were obtained by grinding a mixture of Ce（SO4）2·4H2O, Ti（SO4）2, and Na4P2O7·10H2O in the presence of surfactant PEG-400 at room temperature, washing the mixture with water to remove soluble inorganic salts, and drying at 100℃. The products and their calcined samples were characterized using ultraviolet-visible spectroscopy （UV-vis）, thermogravimetry and differential thermal analyses （TG/DTA）, X-ray powder diffraction （XRD）, and transmission electron microscopy （TEM）. The results show that nano-sized Ce1-xTixP2O7 behave as an excellent UV-shielding material. Thereinto, the CeP2O7 has the most excellent UV-shielding effect, and the amorphous state of Ce0.8Ti0.2P2O7 can keep at a higher temperature than CeP2O7. Therefore, the stabilization of the amorphous state of the cerium pyrophosphates was carded out by doping titanium. This stabilization is a significant improvement, which enables to apply these amorphous pyrophosphates not only to cosmetics and paints, but also plastics and films.Nano-sized cerium-titanium pyrophosphates Ce1-xTixP2O7 （with x = 0, 0.2, 0.5, 0.7, 0.9, and 1.0） were obtained by grinding a mixture of Ce（SO4）2·4H2O, Ti（SO4）2, and Na4P2O7·10H2O in the presence of surfactant PEG-400 at room temperature, washing the mixture with water to remove soluble inorganic salts, and drying at 100℃. The products and their calcined samples were characterized using ultraviolet-visible spectroscopy （UV-vis）, thermogravimetry and differential thermal analyses （TG/DTA）, X-ray powder diffraction （XRD）, and transmission electron microscopy （TEM）. The results show that nano-sized Ce1-xTixP2O7 behave as an excellent UV-shielding material. Thereinto, the CeP2O7 has the most excellent UV-shielding effect, and the amorphous state of Ce0.8Ti0.2P2O7 can keep at a higher temperature than CeP2O7. Therefore, the stabilization of the amorphous state of the cerium pyrophosphates was carded out by doping titanium. This stabilization is a significant improvement, which enables to apply these amorphous pyrophosphates not only to cosmetics and paints, but also plastics and films.

关 键 词：cerium pyrophosphate titanium pyrophosphate solid-state reaction at room temperature UV absorbency stabilization 

分 类 号：TF84[冶金工程—有色金属冶金]