不锈钢/碳钢爆炸复合板消除应力热处理  

THE HEAT TREATMENT OF THE RESIDUAL STRESS RELIEVED FOR EXPLOSIVE WELDED STAINLESS STEEL/CARBON STEEL CLADDED PLATE

作　　者：王治平[1] 何智[1] 李强[1] 高国庆[2] 

机构地区：[1]中物院流体物理研究所冲击波物理与爆轰物理实验室 [2]西南交通大学材料系

出　　处：《高压物理学报》1998年第1期60-66,共7页Chinese Journal of High Pressure Physics

摘　　要：为了消除爆炸焊接不锈钢／碳钢复合板界面的残余应力，对实验样品进行了消除应力热处理，并做了力学性能测试、显微硬度测量、扫描电镜分析和金相分析。结果表明，不论是否经过热处理，界面两侧的成分都有互扩散发生；热处理温度小于５５０℃时，力学性能、金相组织和显微硬度变化不大；热处理温度高于６５０℃时，硬度曲线下降到接近原材的硬度，但同时界面近区碳钢表层发生脱碳现象；热处理温度在７５０℃时，碳钢内部还发生相变。因此不锈钢／碳钢复合板的最佳热处理温度可能在６００℃左右。The　heat　treatment　of　explosive　welded　stainless　steel/carbon　steel　cladded　plates　were　conducted　in　order　to　relieve　the　residual　stress　near　the　welded　interface.The　mechanical　performences　of　the　samples　and　the　microhardness　curves　of　both　sides　of　interface　were　measured.The　composition　of　both　sides　near　the　interface　were　analysed　by　the　scanning　electron　microscope　and　the　metalloscopy.The　results　indicate　that　whether　the　sample　is　heattreated　or　not,the　compositions　of　both　sides　of　the　interface　are　diffused　each　other;When　the　heattreated　temperature　below　550℃,the　mechanical　propertives　and　hardness　of　the　samples　do　not　change　much.When　the　temperature　above　650℃,the　hardness　reduces　but　the　decarburization　of　carbon　steel　in　taken　placed.At　750℃,the　phase　change　is　taken　place　in　the　carbon　steel.Consequently,the　optimum　heattreated　temperature　is　possibly　600℃.

关 键 词：爆炸复合 热处理 残余应力 不锈钢/碳钢 

分 类 号：TG392[金属学及工艺—金属压力加工] TG161