高直流电场下PET薄膜的电致发光及电流特性  

The Study on Electroluminescence and Current Characters of PET Films under High Dc Fields

作　　者：林家齐[1] 王玮[1] 倪海芳[1] 王晨[1] 

机构地区：[1]哈尔滨理工大学应用科学学院,黑龙江哈尔滨150080

出　　处：《哈尔滨理工大学学报》2009年第1期106-107,111,共3页Journal of Harbin University of Science and Technology

基　　金：国家自然科学基金重点项目(50137010);黑龙江省自然科学基金资助项目(E2001-03);黑龙江省教育厅科学技术研究项目(11531029)资助

摘　　要：采用哈尔滨理工大学自主研制的设备测试了高直流电场下PET薄膜电致发光（EL）的光谱、光强和电流特性曲线．实现了电致发光和电导电流特性两种方法的联合测量．通过实验得出：PET的EL发光强度和电流都随着电场的增加而增大，且在外加电场增大到3．5MV／cm后其现象特别明显．EL光谱峰值出现在300～400nm、400—460nm、500～600nm峰带之间．In this paper, the home -made equipment set- up was used to test the EL spectra, light intensity and current characters of PET films under high DC Fields. It makes the measurement that combines the EL and the Current come true. The result shows that both the EL and the current increase with the electric fields, and the phenomena is obvious after the field increased to 3.5 MV/cm. The EL spectra have peaks about 300 - 400 nm, 400 - 460 nm,500 -600 nm.