Nano－ATH的表面改性及其在ABS中的应用  

Study on the Surface Modification of Nano-ATH and Its Application in ABS

作　　者：崔文广[1] 高岩磊[1] 王玉环[2] 李英[1] 任蕾[1] 

机构地区：[1]石家庄学院化工学院,河北石家庄050035 [2]石家庄职业技术学院化工系,河北石家庄050081

出　　处：《塑料科技》2009年第3期64-66,共3页Plastics Science and Technology

基　　金：石家庄市科技支撑计划项目(07107671)

摘　　要：选用钛酸酯偶联剂对纳米氢氧化铝(nano-ATH)进行表面改性,以改善其在丙烯腈-丁二烯-苯乙烯共聚物(ABS)中的分散性。利用透射电镜(TEM)表征了nano-ATH的改性效果,研究了改性条件对nano-ATH/ABS复合材料性能的影响。结果表明:在偶联剂用量2.5%,改性时间25min,改性温度80℃的条件下,nano-ATH/ABS复合材料的综合性能较好,改性后nano-ATH的分散性得到改善。Nano-ATH was modified by titanate coupling agent in order to improve its dispersion in ABS. The modified effect of nano-ATH was analyzed by TEM, and the effects of modification conditions on the properties of nano-ATH/ABS composite were studied. The results showed that the comprehensive properties of nano-ATH/ABS composite were optimum when nano-ATH was modified by 2.5% coupling agent for 25min at 80℃. The dispersion of modified nano-ATH was better than that of unmodified nano-ATH.

关 键 词：纳米氢氧化铝 表面改性 丙烯腈-丁二烯-苯乙烯共聚物 