压力诱导流动成型聚苯乙烯的研究  

Study on Polystyrene Prepared by Pressure Induced Flow Processing

作　　者：梁燕[1] 韩克清[1] 滕翠青[1] 余木火[1] 李书同[1] 金亮[1] 

机构地区：[1]东华大学材料科学与工程学院,纤维材料改性国家重点实验室,上海201620

出　　处：《塑料工业》2009年第3期47-51,共5页China Plastics Industry

基　　金：国家自然科学基金资助(编号50573010;20504006)

摘　　要：以热塑性弹性体SBS作为增容剂,对SBS/聚苯乙烯(PS)的共混物进行压力诱导流动成型,研究了压力诱导流动成型后聚苯乙烯的微观结构和力学性能。结果表明,压力诱导流动成型使聚苯乙烯形成微观层状结构,该结构可以大幅度提高聚苯乙烯的力学性能,缺口冲击强度由8kJ/m2提高到压力诱导流动成型后的30kJ/m2,同时共混物的拉伸强度也有提高。With thermoplastic elastomer prepared by pressure-induced flow processing （ SBS ） （PIFP）. as compatibilizer, SBS/polystyrene （PS） blend was Macro-properties and micro-morphology of polystyrene obtained by PIFP were studied. SEM images showed that micro-sheet structure could be formed via this process. And mechanical properties of SBS/PS were greatly enhanced by formation of this micro-sheet structure. For example, the notched impact strength of SBS/PS increased from 8kJ/m^2 to 30kJ/m^2, the tensile strength also greatly increased compared to the blends obtained by injection.

关 键 词：聚苯乙烯 热塑性弹性体SBS 微观层状结构 压力诱导流动成型 

分 类 号：TQ325.2[化学工程—合成树脂塑料工业]