加成型室温硫化硅橡胶补强研究  

Reinforcing of additional room temperature vulcanizing silicone rubber

作　　者：陈婷 胡飞[2] 戴宏程 王卫华 俞青松 

机构地区：[1]上海回天化工新材料有限公司,上海201600 [2]武汉工程大学绿色化工过程省部共建教育部重点实验室,湖北武汉430073

出　　处：《粘接》2009年第3期42-45,共4页Adhesion

摘　　要：以乙烯基硅油(SiVi)、含氢硅油(SiH)为主要原料,合成了可室温硫化的液体硅橡胶。分析了SiVi与SiH比例、几种补强材料、MQ树脂的合成工艺以及用量对硅橡胶性能的影响。结果表明,当n_(SiH):n_(SiVi)=1.3,MQ树脂用量为25份时,硅橡胶的拉伸强度为2.32 MPa,断裂伸长率为110%。Additional room temperature vulcanizing silicone rubber was prepared with vinyl silicone oil（SiVi） and （SiH） as the raw materials. The influence of mol ratio of SiVi/SiH,several reinforcing fillers, synthetic process and amount of MQ silicone resin was investigated.The results showed that the properties was the best when the nSiH ： nSiVi was 1.3 ： 1 and the amount of MQ silicone resin was 25% by weight;the tensile strength was 2.32 MPa and the elongation at break was 110%.

关 键 词：MQ硅树脂 加成型硅橡胶 室温硫化 

分 类 号：TQ433.438[化学工程]