SH150型双臂吊环裂纹成因分析  

Cause Analysis of Cracks on SH150 Elevator Link

作　　者：吴敏[1] 丁小军 孙小华[1] 邹隽[1] 王燕[1] 张园[1] 

机构地区：[1]三峡大学机械与材料学院,湖北宜昌443002 [2]Sevan Marine Sevan 300项目组,江苏南通226000

出　　处：《石油矿场机械》2009年第3期65-67,共3页Oil Field Equipment

摘　　要：为分析某在役SH150型双臂吊环与大钩连接处阶梯状裂纹群的成因,对该吊环进行了宏观检验及化学成分、力学性能、金相组织分析。结果表明,吊环存在表面脱碳层,使用时存在偏磨是导致吊环表面开裂的主要原因。In order to analyze cause of stepladder cracks on the joint of a SH150 elevator link with hook, the elevator link was investigated using macroscopic examination, chemical composition analysis, metallographic analysis and mechanical properties test. It was showed that decarburized layer existed on the surface of elevator link and inhomogeneous wear on service were the main causes.

关 键 词：吊环 裂纹 偏磨 脱碳层 