载银纳米TiO_2有机表面改性的研究  

Study on Organic Surface Modification of Silver Loaded Nanometer Titanium Dioxide

作　　者：刘云超[1] 彭兵[1] 柴立元[1] 刘立强[1] 李国良[1] 

机构地区：[1]中南大学冶金科学与工程学院,长沙410083

出　　处：《材料导报（纳米与新材料专辑）》2008年第3期82-85,共4页

基　　金：湖南省科技计划重点项目(04GK 2007)

摘　　要：采用硬脂酸对以硫酸氧钛为原料制备的载银纳米TiO_2粉体进行有机表面改性,研究了改性剂用量、改性剂浓度、改性时间、改性温度以及改性pH值的影响,利用红外谱图(FT-IR)、扫描电子显微镜(SEM)等对粒子进行了表征,并检测了其抗菌性能。结果表明,最佳的改性条件下粉体的亲油化度值可达到66.3%,硬脂酸化学键合在粉体的表面,虽抗菌率略有下降,但仍能达到99.77%。The organic surface modification of Ag loaded TiO2 by the stearic acid is investigated. The effects of the reagent amount, concentration, modification time, temperature and pH value are determined. The prepared samples are characterized by FT-IR, SEM techniques, and the antibacterial property is determined. The results show that the lipophilic degree reaches up to 66. 3% under optimal conditions. The stearic acid is bound on the surface of Ag loaded TiO2 by chemical bond. Although the antibacterial rate decreases slightly, it still achieves 99. 77%.

关 键 词：载银 纳米TIO2 硬脂酸 有机改性 

分 类 号：TQ426.81[化学工程] TG174.444[金属学及工艺—金属表面处理]