聚苯并噁嗪基高导电复合材料的电性能研究  

Study on Electrical Behavior of Polybenzoxazine Conductive Composites

作　　者：刘勇[1,2] 邓建国[1] 朱敬芝[1] 曹琼华[1,2] 罗雪方[1,3] 纪兰香[1,3] 白战争[1,3] 

机构地区：[1]中国工程物理研究院化工材料研究所 [2]96411部队25分队 [3]西南科技大学材料学院

出　　处：《材料导报（纳米与新材料专辑）》2008年第3期264-265,268,共3页

摘　　要：采用片状石墨(GP)、短切碳纤维(SCF),利用高温模压复合的方法,制得高固含量的聚苯并噁嗪/GP/CF导电复合材料(Φc>80%),通过分析导电填料GP丙酮溶剂化处理前后的红外谱图变化,以及导电填料GP和SCF的复配前后材料体积电阻率变化,研究了导电性有明显差异的原因。Polybenzoxazine/expanded graphite（GP）/short carbon fiber（SCF）conductive composites were prepared, by employing the molding composite-method at high temperature, when the percolation threshold （φc）〉80%. The changes of conductive fillers（GP）by acetone solvent-treatment in the infrared spectrum（IR）, and the difference between the fillers GP and SCF grading on the composites before and after is investigated. The essential reasons causing the evident difference in φc and conductivity of the composites prepared via different methods are studied.

关 键 词：聚苯并噁嗪 溶剂化处理 导电填料 电阻率 

分 类 号：TQ323.1[化学工程—合成树脂塑料工业] TM243[一般工业技术—材料科学与工程]