A cluster line approach to finding new Fe-B-Y-Nb-Zr bulk metallic glasses  

作　　者：Nigel Pemberton-Pigott 

机构地区：[1]State Key Laboratory of Materials Modification, Dalian University of Technology

出　　处：《International Journal of Minerals,Metallurgy and Materials》2007年第S1期26-30,共5页矿物冶金与材料学报（英文版）

基　　金：This project was financially supported by the National Natural Science Foundation of China (No.50401020, 50671018, 50631010);the Provincial Science and Technology Foundation of Liaoning, China.

摘　　要：The glass forming ability of the [(Fe12/13Y1/13)100?xBx]96Nb2Zr2 (x=9–26) system was investigated using a series of cluster lines. Three types of clusters, an icosahedron (Fe12Y), a capped Archimedes anti-prism (Fe8B3) and a capped trigonal prism (Fe9B), as well as a binary eutectic (Fe83B17) were considered. Bulk glassy alloy rods of 3 mm in diameter were synthesized using a copper mold suction-casting method. The glass transition temperature was observed for all samples in the boron range of 15.9at%-25.7at%, with the alloy at 15.9at% of boron having the best thermal properties. The ferrous-based bulk metallic glasses (BMG) obtained have high reduced glass transition temperatures with the maximum reaching 0.63 and large supercooled liquid regions with the maximum reaching 111 K. Magnetic testing revealed a large value of coercive force and remanent magnetization, being 11 kA/m and 0.1 T, re- spectively.The glass forming ability of the [(Fe12/13Y1/13)100?xBx]96Nb2Zr2 (x=9–26) system was investigated using a series of cluster lines. Three types of clusters, an icosahedron (Fe12Y), a capped Archimedes anti-prism (Fe8B3) and a capped trigonal prism (Fe9B), as well as a binary eutectic (Fe83B17) were considered. Bulk glassy alloy rods of 3 mm in diameter were synthesized using a copper mold suction-casting method. The glass transition temperature was observed for all samples in the boron range of 15.9at%-25.7at%, with the alloy at 15.9at% of boron having the best thermal properties. The ferrous-based bulk metallic glasses (BMG) obtained have high reduced glass transition temperatures with the maximum reaching 0.63 and large supercooled liquid regions with the maximum reaching 111 K. Magnetic testing revealed a large value of coercive force and remanent magnetization, being 11 kA/m and 0.1 T, re- spectively.

关 键 词：bulk metallic glasses Fe-B-Y-Nb-Zr alloys composition design cluster line 

分 类 号：TG139.8[一般工业技术—材料科学与工程]