Effect of Rare Earths on Structure and Properties of Carbonitriding Boronizing Combined Treatment  

作　　者：叶宏 闫忠琳 田中青 

机构地区：[1]School of Materials Science and Engineering, ChongqingInstitute of Technology

出　　处：《Journal of Rare Earths》2007年第S1期415-418,共4页稀土学报（英文版）

基　　金：the Natural Science Foundation of Chongqing (2006BB4391)

摘　　要：The microstructure, thickness, microhardness and wear resistance of single-boronizing, carbonitriding+boronizing and carbonitriding+RE-boronizing layers of 16Mn steel were investigated respectively. Effect of rare earths on microstructure and properties of the penetrated layer were studied and the mechanism of effects of rare earths was discussed. The result showed that the structure, microhardness, brittleness and wear resistance of the penetrated layer after carbonitriding+ RE-boronizing were better than that of conventional boronizing and carbonitriding, especially the wear resistance of boronized layer was increased remarkably. The RE-boronizing layer of the steel is single phase Fe2B, and RE elements enhanced Fe2B (002) direction texture. The distribution of rare earth element (La) in the layer was non-uniform. RE content is higher between borides than that of the interior of borides. An optimum value of the addition of RE element in the agent was 8%. The average service life of the 16Mn steel brick mould treated by carbonitriding+RE-boronizing was 1.5 times as long as the service life of the mould treated by carbonitriding-boronizing.The microstructure, thickness, microhardness and wear resistance of single-boronizing, carbonitriding+boronizing and carbonitriding+RE-boronizing layers of 16Mn steel were investigated respectively. Effect of rare earths on microstructure and properties of the penetrated layer were studied and the mechanism of effects of rare earths was discussed. The result showed that the structure, microhardness, brittleness and wear resistance of the penetrated layer after carbonitriding+ RE-boronizing were better than that of conventional boronizing and carbonitriding, especially the wear resistance of boronized layer was increased remarkably. The RE-boronizing layer of the steel is single phase Fe2B, and RE elements enhanced Fe2B (002) direction texture. The distribution of rare earth element (La) in the layer was non-uniform. RE content is higher between borides than that of the interior of borides. An optimum value of the addition of RE element in the agent was 8%. The average service life of the 16Mn steel brick mould treated by carbonitriding+RE-boronizing was 1.5 times as long as the service life of the mould treated by carbonitriding-boronizing.

关 键 词：BORONIZING CARBONITRIDING structure PROPERTIES rare earths 

分 类 号：TG156.87[金属学及工艺—热处理]