Preparation of PbTiO_3 Conductive Powders and Coatings  

作　　者：王威力 郝素娥 王春艳 

机构地区：[1]Department of Applied Chemistry, Harbin Institute of Technology

出　　处：《Journal of Rare Earths》2007年第S1期561-564,共4页稀土学报（英文版）

基　　金：the National Natural Science Foundation of China (20571020)

摘　　要：La2O3 and Ce2O3 were penetrated into PbTiO3 to obtain conductive powders, and then they were mixed with polyurethane and butyl acetate to prepare conductive coatings. The results showed that the electric property of modified PbTiO3 powders was improved by penetration of La2O3 and Ce2O3. XRD patterns showed that some new compounds such as La2Ti6O15, CeTi21O38 and Pb0.634La0.209Ti0.948O2.284 were formed, which led to the rapid increase of conductivity. The resistivity of modified PbTiO3 powders decreased to 3.88 Ω·m. The coatings using modified PbTiO3 powders as fillings also had a good conductivity. When the PbTiO3 powders were 10% and antisettle agent (bentonite) content was 0.50%, and mass ratio between polyurethane and butyl acetate was 1.05, the surface resistivity of the coatings fell down to 1.3×108 Ω·m. This kind of conductive coatings could be used in electromagnetic shielding.La2O3 and Ce2O3 were penetrated into PbTiO3 to obtain conductive powders, and then they were mixed with polyurethane and butyl acetate to prepare conductive coatings. The results showed that the electric property of modified PbTiO3 powders was improved by penetration of La2O3 and Ce2O3. XRD patterns showed that some new compounds such as La2Ti6O15, CeTi21O38 and Pb0.634La0.209Ti0.948O2.284 were formed, which led to the rapid increase of conductivity. The resistivity of modified PbTiO3 powders decreased to 3.88 Ω·m. The coatings using modified PbTiO3 powders as fillings also had a good conductivity. When the PbTiO3 powders were 10% and antisettle agent (bentonite) content was 0.50%, and mass ratio between polyurethane and butyl acetate was 1.05, the surface resistivity of the coatings fell down to 1.3×108 Ω·m. This kind of conductive coatings could be used in electromagnetic shielding.

关 键 词：PbTiO_3 conductive powder conductive coating rare earths 

分 类 号：O614.3[理学—无机化学]