SYNTHESIS AND PROPERTIES OF ANILING ANILING AND 0-AMINOBENZENESULFONIC ACID COPOLYMER  

作　　者：Jun-hua Fan Mei-xiang Wan Dao-ben Zhu Institute of Chemistry, Chinese Academy of Sciences, Beijing 100080, China 

出　　处：《Chinese Journal of Polymer Science》1999年第2期165-170,共6页高分子科学（英文版）

基　　金：The project was supported by National Natural Science Foundation of China, the National Advanced Materials Committee of China(NAMCC)and Chinese Academy of Sciences.

摘　　要：Poly(aniline- co-o-aminobenzenesulfonic acid) (PAOABSA) as a water soluble conducting polymerwas synthesized by chemical polymerization. The productivity and the room-temperature conductivity of thecopolymer were measured as a function of the reaction conditions, such as reaction temperature, the ratio ofoxidant to monomer and the degree of sulfonation defined as the ratio of sulfur to nitrogen atoms(S/N). Themain results obtained are summarized as follows : (1) lower reaction temperature (at about 0℃) is favorablefor the enhancement of the room-temperature conductivity of the copolymer; (2) higher content of oxidant isunfavorable for increasing the room-temperature conductivity of the copolymer; (3) both productivity androom-temperature conductivity of the copolymer decrease with increase of the degree of sulfonation whichwas always lower than 0.5 even an excess of o-aminobenzenesulfonic acid was added, probably because thereactivity ratio of aniline (γ=2.99± 0.05) is much higher than that of o-aminobenzenesulfonic acid (γ_2 = 0.06±0.02) estimated by using Fineman-Ross method and least square method.Poly(aniline- co-o-aminobenzenesulfonic acid) (PAOABSA) as a water soluble conducting polymerwas synthesized by chemical polymerization. The productivity and the room-temperature conductivity of thecopolymer were measured as a function of the reaction conditions, such as reaction temperature, the ratio ofoxidant to monomer and the degree of sulfonation defined as the ratio of sulfur to nitrogen atoms(S/N). Themain results obtained are summarized as follows : (1) lower reaction temperature (at about 0℃) is favorablefor the enhancement of the room-temperature conductivity of the copolymer; (2) higher content of oxidant isunfavorable for increasing the room-temperature conductivity of the copolymer; (3) both productivity androom-temperature conductivity of the copolymer decrease with increase of the degree of sulfonation whichwas always lower than 0.5 even an excess of o-aminobenzenesulfonic acid was added, probably because thereactivity ratio of aniline (γ=2.99± 0.05) is much higher than that of o-aminobenzenesulfonic acid (γ_2 = 0.06±0.02) estimated by using Fineman-Ross method and least square method.

关 键 词：Watersoluble polyaniline Reactivity ratio COPOLYMER 

分 类 号：TQ317.6[化学工程—高聚物工业]