含H2S井钻铤本体断裂原因分析  

Analysis of Drill Collar Fracture in a Well with H_2S

作　　者：吕拴录[1,2] 李金凤[3] 江涛[1] 迟军[2] 谢居良[2] 巨西民[3] 

机构地区：[1]塔里木油田,库尔勒841000 [2]中国石油大学,北京102249 [3]中国石油天然气集团公司管材研究所,西安710065

出　　处：《腐蚀与防护》2009年第4期283-284,287,共3页Corrosion & Protection

摘　　要：对某井ф120.7 mm钻铤断裂事故进行了调查研究,对钻铤材质、断口和裂纹形貌进行了试验分析。结果表明:钻铤材料符合SY/T5144-1997标准要求,钻铤裂纹和断口位置的硫含量远高于其它部位,钻铤断裂为H2S导致的应力腐蚀开裂(SSCC)。The drill collar fracture accident in a H2S-containing well was studied. The fracture showed intergranular morphology and the sulfur content was higher in the cracks than that in the other area of the drill collar. It is concluded that the drill collar material is in accordance with SY/T 5144--1997 standard requirement, and the fracture resulted from sulfide stress corrosion crack （SSCC）.

关 键 词：钻铤 H2S 应力腐蚀开裂 沿晶断口 

分 类 号：TG172.8[金属学及工艺—金属表面处理]