加工工艺对稀土HSn62-1黄铜耐脱锌腐蚀性能的影响  

The Effect of Processing Techniques on Corrosion Resistance of RE HSn62-1 Brass

作　　者：刘坚锋[1] 陈一胜[1] 朱志云[1] 刘永丹[1] 

机构地区：[1]江西理工大学材料与化学工程学院,江西赣州341000

出　　处：《铝加工》2009年第2期24-26,共3页Aluminium Fabrication

摘　　要：采用脱锌腐蚀深度测量方法、恒电位测试方法和光学显微镜等分析方法,研究了不同的加工工艺对稀土HSn62-1黄铜的耐脱锌腐蚀性能的影响。结果表明,冷轧态的黄铜,由于β相沿着冷加工方向分布,同时位错密度和残余应力的增加,导致了其耐脱锌腐蚀性能比热轧态的黄铜和铸造态的黄铜差。热轧态的黄铜,由于在热加工过程中发生了回复和再结晶,使得其耐蚀性和铸造态的相当。The effect of various prcessing techniques on corrosion resistance of RE HSn62-1 brass were investigated using dezincifieation corrosion depth testing, potential tests and optical mieroscope. The results show that dezineification corrosion resistance of cold-rolled RE HSn62-1 brass is worse than that of hot-rolled brass and as-cast brass due to β phase distributed along cold-working direction and the increase of dislocation density and residual stress. The corrosion resistance of hot-roiled brass is equivalent to that of as-cast brass due to dynamic recovery and recrystallization during hot rolling.

关 键 词：稀土HSn62-1黄铜 热轧 冷轧 耐脱锌腐蚀 电化学 

分 类 号：TG172[金属学及工艺—金属表面处理]