PVC/NBR再生胶共混型热塑性弹性体的研究  

Study on PVC/RNBR blended thermoplastic elastomer

作　　者：张军[1] 钱润男[1] 秦志英 刘巍然 

机构地区：[1]南京化工大学高分子系

出　　处：《合成橡胶工业》1998年第3期168-171,共4页China Synthetic Rubber Industry

摘　　要：用ＰＶＣ与ＮＢＲ再生胶高温机械共混，制备了具有交联结构的、Ｔｇ约１０℃的热塑性弹性体。讨论了共混比、第三组分改性剂合成橡胶（ＮＢＲ，ＰＵ，ＣＲ，ＣＰＥ）、５种硫化体系、填充剂（炭黑、白炭黑、重质ＣａＣＯ３）、增塑剂邻苯二甲酸二辛酯等因素对性能的影响。结果表明：ＰＶＣ６０份，ＮＢＲ再生胶４０份，ＮＢＲ３６０４２０份，硫磺０．５份，促进剂ＴＭＴＤ和促进剂ＣＺ各０．６～０．９份及适量重质ＣａＣＯ３和增塑剂，可制得综合性能较好的共混型热塑性弹性体。The polyvinyl chloride(PVC)/reclaimed acrylonitrile-butadiene rubber (RNBR)blended thermoplastic elastomer was prepared by mechanical blending at high temperature.The effects of blending ratio of PVC/RNBR,synthetic rubber modifiers(NBR,PU,CR,CPE),curing systems,fillers(carbon black,silica,calcium carbonate)and content of plasticizer di-2-ethylhexyl phathalate on the mechanical properties of the thermoplastic elastomer were discussed.The results showed that PVC/RNBR blended thermoplastic elastomer with optimum properties were obtained using PVC 60 phr,RNBR 40 phr,NBR 20 phr , sulfur 0.5 phr , accelerator TMTD 0.6～0.9 phr,accelerator CZ 0.6～0.9 phr,calcium carbonate 15 phr and some plasticizer.The glass transition temperature of thermoplastic elastomer was 10 ℃.

关 键 词：聚氯乙烯 丁腈橡胶 再生胶 共混型 热塑性弹性体 

分 类 号：TQ334.9[化学工程—橡胶工业]