Enhanced Magnetoresistance of （La0.67Ca0.33MnO3） Composites Coated by Zn0.95Co0.05O  

作　　者：庄彬 徐妍 赖恒 黄志高 陈水源 林应斌 李山东 赖发春 

机构地区：[1]Department of Physics, Fujian Normal University, Fuzhou 350007

出　　处：《Chinese Physics Letters》2009年第5期224-227,共4页中国物理快报（英文版）

摘　　要：La0.7Ca0.3MnO3：xZn0.95Co0.05O （x=0.0,0.05, 0.1, 0.15mol） composites are prepared by a sol-gel process. X- ray diffraction and energy diffraction spectroscopy reveal that there is no evidence of a reaction between the La0.7 Ca0.3 MnO3 （LCMO） and Zn0.95Co0.05 O （ZCO）. Magnetization M, Curie temperature Tc and metal-insulator transition temperatures Tp are observed to decrease with increasing ZCO content. Compared with x = 0.0, a great enhancement in the magnetoresistance （MR） is observed at around Tc for x = 0.05, 0.10, 0.15. Based on the tunneling MR and percolation models, this great change of MR is well explained.La0.7Ca0.3MnO3：xZn0.95Co0.05O （x=0.0,0.05, 0.1, 0.15mol） composites are prepared by a sol-gel process. X- ray diffraction and energy diffraction spectroscopy reveal that there is no evidence of a reaction between the La0.7 Ca0.3 MnO3 （LCMO） and Zn0.95Co0.05 O （ZCO）. Magnetization M, Curie temperature Tc and metal-insulator transition temperatures Tp are observed to decrease with increasing ZCO content. Compared with x = 0.0, a great enhancement in the magnetoresistance （MR） is observed at around Tc for x = 0.05, 0.10, 0.15. Based on the tunneling MR and percolation models, this great change of MR is well explained.

分 类 号：O482.5[理学—固体物理] TG174.442[理学—物理]