TIG熔修对船体钢焊接接头低温脆断性能的影响  

Effects of TIG Weld Dressing on Low Temperature Brittle Fracture Resistance of Welded Joint of Hull Steels

作　　者：朱梅五[1] 殷沐德[1] 

机构地区：[1]海军工程学院

出　　处：《材料开发与应用》1998年第2期20-22,共3页Development and Application of Materials

摘　　要：通过落锤试验，对经ＴＩＧ熔修和未经ＴＩＧ熔修的４４０ＭＰａ级、５９０ＭＰａ级船体用钢焊接接头的低温脆断特性进行了较为全面的研究。结果显示，ＴＩＧ熔修对不同钢种、不同形式接头的低温性能有着不尽相同的作用效果，其中４４０ＭＰａ级船体钢Ｔ型接头经熔修处理后，其低温脆断抗力得到了十分显著地提高。For two hull steel with strengths of 590 MPa and 440 MPa, the effects of TIG weld dressing on the low temperature brittle fracture resistance of welded joints were investigated respectively through drop weight tests. The results show that the effects of TIG weld dressing are different according to the steel grades and joint types, and the low temperature brittle resistance of T joint of 440MPa steel was obviously increased by TIG weld dressing.

关 键 词：TIG熔修 焊接接头 低温脆性 船体 钢 

分 类 号：U672.1[交通运输工程—船舶及航道工程]