EDTA对纳米γ-Al_2O_3浆料分散性能的影响  

Effect of EDTA on nanometer γ-Al_2O_3 slurry dispersivity

作　　者：张开明[1] 褚立华[1] 刘超峰[1] 郑峰[1] 

机构地区：[1]中南大学材料科学与工程学院,长沙410083

出　　处：《粉末冶金材料科学与工程》2009年第2期110-114,共5页Materials Science and Engineering of Powder Metallurgy

基　　金：中南大学本科生创新实验基金(LA06018)

摘　　要：为了分析有机小分子对纳米粉末分散性的影响,通过一系列沉降实验,研究有机乙二胺四乙酸(EDTA)对纳米γ-Al2O3浆料的分散效果。测定浆料的Zeta电位-pH曲线,并确定其等电位点。使用激光粒度分析仪对比分析EDTA及pH值对浆料粒度的影响;利用傅立叶变换红外光谱(FT-IR)试验验证浆料颗粒的表面化学吸附现象,探讨EDTA的分散机理。实验结果表明,EDTA化学吸附到浆料颗粒的表面,通过颗粒间的静电斥力起到很好的分散作用。Ethyl enediamine tetra acetic acid （EDTA） was used to disperse nanometer-alumina （γ-Al2O3） slurry and its chemical absorption and dispersive effect as a function of pH was investigated by sedimentation experiments, zeta potential measurement, particle size analysis and Fourier Transform Infrared （FT-IR） spectrometry respectively. The mechanism associated with dispersion of EDTA has been discussed based on experimental results. The results indicated that slurry particles are dispersed by their electrostatic repulsive force through the chemical absorption of EDTA.

关 键 词：EDTA 分散 纳米γ-Al2O3浆料 化学吸附 

分 类 号：TB559[理学—物理]