1420铝锂合金的晶粒细化及超塑性行为  

Grain Refinement and Superplastic Behavior of 1420 Al-Li Alloy Sheets

作　　者：张新明[1] 叶凌英[1] 郑大伟[1] 

机构地区：[1]中南大学材料科学与工程学院

出　　处：《航空制造技术》2009年第10期82-86,共5页Aeronautical Manufacturing Technology

基　　金：国际科技合作重点项目(2008DFR50260);国家重大基础研究项目(2005CB623706)资助

摘　　要：采用一种新型形变热处理方法制备1420铝锂合金细晶超塑性板材,其再结晶平均晶粒尺寸约7μm。对细晶板材在温度范围450～570℃、应变速率5×10^(-4)～1×10^(-2)s^(-1)条件下进行高温超塑性拉伸,探求了对板材流动行为及组织演变的影响规律。在525℃和1×10^(-3)s^(-1)同的变形条件下,板材呈现了最高延伸率,约为915%。Fine grained superplastic 1420 Al-Li alloy sheets are produced by a novel thermo-mechanical processing, which obtains an average grain diameter of approximate 7μm. Superplasticity tests by uniaxial stretching are conducted in the temperature range of 450-570℃ and strain rates range of 5×10^-4-1×10^-2s^-1, and their effects of the temperature and strain rate on flow behavior and microstructural evolution of the sheets are determined investigated. The sheet gets the maximal elongation about 915% on the deformation condition of 525℃ and 1×10^-3s-1.