2B96K铝锂合金剥蚀过程的电化学阻抗研究  

Electrochemical Impedance Spectroscopy during Exfoliation Corrosion Process of 2B96K Al-Li Alloy

作　　者：李昱锜 胡治流[2] 江鸿杰[1] 

机构地区：[1]广西大学机械工程学院,南宁530004 [2]广西大学资源与环境学院,南宁530004

出　　处：《腐蚀与防护》2009年第5期312-315,共4页Corrosion & Protection

摘　　要：研究了不同时效状态下的2B96K铝锂合金在EXCO溶液中剥蚀的电化学阻抗特征。结果表明,腐蚀初期,合金的电化学阻抗谱由一个容抗弧及一个感抗弧组成,一旦发生剥蚀,即变成两个容抗弧。对于欠时效合金,这两个容抗弧出现的时间较长,表明其剥蚀发展较慢。对电化学阻抗谱进行了拟合分析,得到了剥蚀的相关信息,如剥蚀的发展及形貌等。The electrochemical impedance spectroscopy （EIS） during exfoliation corrosion process of 2B96K Al-Li alloy with different aging treatments in EXCO solution was studied. At the beginning of corrosion, the EIS was comprised of a capacitive arc and an inductive loop. Once exfoliation corrosion occurred, two capacitive arcs appeared. The longer appearance time of two capacitive arcs of the under-aged alloy indicated its slower corrosion development. The simulated EIS analysis was done, the inforrnation such as developing and feature of exfoliation corrosion was goet.

关 键 词：剥蚀 AL-LI合金 电化学阻抗谱(EIS) 

分 类 号：TG172[金属学及工艺—金属表面处理] TG146.2[金属学及工艺—金属学]