不同工艺对LaFe_(11.9-x)Co_xSi_(1.1)B_(0.25)(x=0.7,0.8)合金的磁热效应的影响  

Effect of Different Producing Method on Magnetocaloric Effects of LaFe_(11.9-x)Co_xSi_(1.1)B_(0.25)(x=0.7,0.8) Alloys

作　　者：郭培亮[1,2] 黄焦宏[2] 金培育[2] 阎宏伟[2] 刘翠兰[2] 邓沅[2] 

机构地区：[1]内蒙古工业大学材料科学与工程学院,内蒙古呼和浩特010051 [2]包头稀土研究院,内蒙古包头014030

出　　处：《稀土》2009年第2期35-38,共4页Chinese Rare Earths

基　　金：内蒙古科技计划项目(20070402)

摘　　要：从室温磁制冷商品化角度出发,用工业纯原料,对用不同工艺(甩带、铸锭)制作的LaFe11.9-xCoxSi1.1B0.25(x=0.7,0.8)合金的磁热效应作了研究。研究结果表明,铸锭样品的磁热效应优于甩带样品,在1.5T磁场下,铸锭LaFe11.2Co0.7Si1.1B0.25样品的温变最大值达到2.6K,对应的温度在-6℃左右。随着Co的加入,居里温度升高,但磁热效应有所降低。Magnetocalorie effects of LaFe11.9-xCoxSi1.1B0.25（x=0.7,0.8）alloys prepared by melt spinning and casting have been investigated. Experimental results reveal that the magnetocaloric effect of melt - spun LaFe11.9-xCoxSi1.1B0.25（x=0.7,0.8） alloy is lower than that of as- east counterparts. The measured maximum of adiabatic temperature change of as - cast LaFe11.2Co0.7Si1.1 Bo,25（x= 0.7） alloy is 2.6K at about - 6℃ .With adding of Co, Curie temperature Tc shifts to high value and the measured adiabatic temperature change decreases.

关 键 词：磁热效应 甩带 铸锭 工业纯 

分 类 号：TG132.27[一般工业技术—材料科学与工程] TM271[金属学及工艺—合金]