离子液体中棒状ZnO粉体的制备及光催化性能  

Preparation,characterization and photocatalytic performance of ZnO rods crystal in ionic liquids

作　　者：于春玲[1,2] 周咏梅[1] 董晓丽[1] 廉锁原[1] 王少君[1] 

机构地区：[1]大连工业大学化工与材料学院,辽宁大连116034 [2]清华大学化学系,北京100084

出　　处：《大连工业大学学报》2009年第3期181-183,共3页Journal of Dalian Polytechnic University

基　　金：国家重点基础研究发展计划(“973”计划)项目(2003CB615805);辽宁省科学技术基金资助项目(1050300);辽宁省教育厅科学研究计划资助项目(202073411)

摘　　要：制备了离子液体1-乙基-3-甲基咪唑溴盐（[emin]Br）,以该离子液体为模板剂,采用水热法制备了亚微米级棒状ZnO粉体。经扫描电子显微镜（SEM）、X射线衍射（XRD）、傅立叶转换红外光谱（FT-IR）等对样品进行了表征和分析。结果表明,该方法制备出具有六方纤锌矿结构的棒状亚微米级ZnO粉体,棒长为2-3μm,直径为500-600 nm;以高压汞灯为光源,以ZnO粉体为光催化剂,对有机染料罗丹明B进行了光降解实验,光降解90 min后,其去除率达到93.3%。ZnO submicron-rods were prepared in ionic liquid solvent of the synthesized 1-heptal-3-methylimidazolium bromide and characterized by SEM.XRD and FT IR. The results showed that the structure of ZnO rods was hexagonal wurtzite in 2-3 μm length and 500-600 nm round. The degradation rate was 93.3% after being irradiated for 90 min when the prepared ZnO rods were applied on photodegradation of Rhodamine B.

关 键 词：离子液体 ZNO 光催化 

分 类 号：TP391.41[自动化与计算机技术—计算机应用技术]